Ecofriendly nanostructured materials have been proposed as promising alternative control means to prevent plant diseases. Chitosan nanoparticles (CN), silica nanoparticles (SN) and chitosan-silica nanocomposites (CSN) were synthesized and their morphology and structure was characterized by transmission electron microscope (TEM), scanning electron microscopy (SEM), infrared spectra (FT-IR) and Raman spectroscopy. Their antifungal efficiency against Botrytis cinerea, the causal fungus of gray mold disease of table grapes, was tested in vitro and in vivo (under artificial and natural infections). In vitro tests showed that CN, SN and CSN reduced fungal growth by 72, 76 and 100%, respectively at 1% as compared to control. Under natural infection, at the end of cold storage, CSN was the most effective treatment, and reduced the development of gray mold by 59 and 83%, for 'Italia' and 'Benitaka' grapes, respectively as compared to the water control. Results indicate that a synergistic effect of CSN against gray mold was observed. The impact of tested nanocomposites on soluble solids - TSS, titratable acidity - TA, TSS/TA, berry color, mass loss, stem browning and shattered berries was investigated. No negative effect of tested nanomaterials in term of grape quality was observed. For 'Italia' table grape, CN and CSN can preserve bunches from mass loss as compared to control. Also, the effect of CSN on reactive species of oxygen (ROS), ATP content and mitochondrial membrane potential (MMP) of B. cinerea spores was determined to verify its mode of action. The obtained results suggested CSN, as alternative control means, to reduce/substitute the use of fungicides to control gray mold of table grapes while maintaining grape quality.
Keywords: Botrytis cinerea; Chitosan-silica nanocomposites; Postharvest and fruit quality.
Copyright © 2019 Elsevier B.V. All rights reserved.