Multi-structured Ag/MnO2-cordierite molded catalysts were prepared by hydrothermal method and applied to the catalytic oxidation of VOCs. Catalytic activities of Ag/MnO2-cordierite were evaluated by 1000 ppm of toluene, ethyl acetate and chlorobenzene degradation respectively at the air atmosphere, and their physicochemical properties were characterized through multiple techniques containing XRD, SEM, TEM, H2-TPR and XPS. It is found that nanorod Ag/MnO2-cordierite molded catalyst showed prominent catalytic activity for VOCs decomposition and the T90 for toluene, ethyl acetate and chlorobenzene are 275 °C, 217 °C and 385 °C respectively under the space velocity of 10,000 h-1. High valence manganese oxide, more active lattice oxygen proportion and superior low-temperature reducibility were the great contributors to the high activity of the catalyst with nanorod morphology. Studies of space velocity and catalytic stability over nanorod Ag/MnO2-cordierite molded catalyst have confirmed the good catalytic performance, excellent mechanical strength and satisfied anti-toxicity to Cl at higher space velocity, which indicates that this molded catalyst have promise for industrial application.