A bark-like imitated polypr opylene (PP)/polycarbonate (PC) nanofibrous membrane was constructed by one-step meltblown technique for efficient particulate matter (PM) removal. The effects of PC content (0%, 1%, 3%, 5%, and 7%) on membrane thermal stability, microscopic characteristics, filtration performance, hydrophilicity, and water vapor transmission were investigated. The results demonstrated that using facile design of incompatibility and viscosity difference between PC and PP polymers decreases average fiber diameter, creating a bark-like groove appearance and increasing surface potential, making a new PP/PC membrane with high filtration performance. The resultant PP/PC membrane had finer average fiber diameter of 0.63 μm, which was nearly 89.41% lower than PP membranes (5.95 μm), and its quality factor (0.036 Pa-1) was nearly 2.12 times than that of PP membranes (0.017 Pa-1) with the die hole diameter of 0.5 mm. This fabrication technique of a special meltblown filter membrane saves the cost of die retrofitting and post-processing, which provides an innovative method for particulate efficient removal of high efficient filters.
Keywords: bark-like imitated; filtration performance; meltblown; nanofibrous; one-step.