Biomaterials-centered infection or implant-associated infection plays critical roles in all areas of medicine with implantable devices. The widespread over use of antibiotics has caused severe bacterial resistance and even super bugs. Therefore, the development of anti-infection implantable devices with non-antibiotic-based new antimicrobial agents is indeed a priority for all of us. In this study, antimicrobial composite meshes were fabricated with broad-spectrum antimicrobial peptides (AMPs). Macroporous polypropylene meshes with poly-caprolactone electrospun nanosheets were utilized as a substrate to load AMPs and gellan gum presented as a media to gel with AMPs. Different amounts of AMPs were loaded onto gellan gum to determine the appropriate dose. The surface morphologies, Fourier-transform infrared spectroscopy spectra, in vitro release profiles, mechanical performances, in vitro antimicrobial properties, and cytocompatibility of composite scaffolds were evaluated. Results showed that AMPs were loaded into the meshes successfully, the in vitro release of AMPs in phosphate-buffered saline was prolonged, and less than 60% peptides were released in 10 days. The mechanical properties of composite meshes were also within the scope of several commercial surgical meshes. Composite meshes with the AMP loading amount of over 3 mg/cm2 showed inhibition against both Gram-negative and Gram-positive bacteria effectively, while they presented no toxicity to mammalian cells even at a loading amount of 10 mg/cm2. These results demonstrate a new simple and practicable method to offer antimicrobial properties to medical devices for hernia repair.
Keywords: antimicrobial composite mesh; antimicrobial peptides; cytocompatibility; implant associated infection; slow release.