A novel corrosion and scale inhibitor (TPP) containing tobacco stem extract (TSE), polyepoxysuccinic acid (PESA), and polyaspartic acid (PASP) was obtained by the optimal proportion of the orthogonal test. The anticorrosion effect of TPP for carbon steel was researched by static weight-loss method, on-line simulated dynamic test, electrochemical measurement, and scanning electron microscopy (SEM). The results showed that TPP could protect carbon steel efficiently with a maximal corrosion inhibition rate of 85.7% and it was a mixed-type corrosion inhibitor, mainly exhibiting cathode suppression capacity. Simultaneously, the results of calcium carbonate deposition experiment indicated that the scale inhibition rate of TPP was up to 100%.
Keywords: carbon steel; corrosion inhibition; electrochemistry; morphology analysis; scale inhibition.