The determination of an appropriate amount of turning for superalloy ingot surfaces, in a scientific and reasonable manner, is vital to the improvement of the metallurgical quality and comprehensive performance of superalloy ingots. In the present study, scanning electron microscopy with energy-dispersive spectroscopy, a high-temperature testing machine, a Brinell hardness tester and the Image-Pro Plus software were used to analyze and compare the types and amounts of inclusions, the average area of the (Al,Mg)O inclusions, and the mechanical properties of points at different distances from the edge of the GH4169 superalloy vacuum arc remelting (VAR) ingot edge. The effects of the amount of turning to which the superalloy is subjected, the metallurgical qualities, and the mechanical properties were systematically studied. The results showed that the five inclusion types did not change as the sampling locations moved away from the ingot edge, but the amount of inclusions and the average area of the (Al,Mg)O inclusions first decreased and then stabilized. Similarly, the tensile strength, elongation, section shrinkage, hardness, and fatigue life first increased and then stabilized. Finally, this experiment tentatively determined that an appropriate amount of turning for a GH4169 superalloy ingot is 36-48 mm.
Keywords: GH4169 superalloy; inclusions; mechanical properties; turning amount; vacuum arc remelting.