This paper presents an experimental study on the dynamic compressive behaviour of polypropylene (PP) fibre reinforced concrete under various strain rates using split Hopkinson pressure bar (SHPB) equipment. The effects of PP fibre content and strain rate on the dynamic compressive stress-strain relationship and failure patterns were estimated. The results indicated that the addition of PP fibre enhanced the dynamic compressive properties of concrete mixtures although it resulted in a significant reduction in workability and a slight decrease in static compressive strength. Considering the workability, static compressive strength and dynamic compressive behaviour, the optimal PP fibre content was found to be 0.9 kg/m3 as the mixture exhibited the highest increase in dynamic compressive strength of 5.6%, 40.3% in fracture energy absorption and 11.1% in total energy absorption; further, it showed the least reduction (only 5.8%) in static compressive strength among all mixtures compared to the reference mixture without fibre. For all mixtures, the dynamic compressive properties, energy absorption capacity, strain at peak stress, ultimate strain and dynamic increase factor (DIF) were significantly influenced by strain rate, i.e., strain rate effect. When the strain rate was relatively low, PP fibres were effective in controlling the cracking, and the dynamic compressive properties of PP fibre reinforced mixtures were improved accordingly.
Keywords: Fibre reinforced concrete; constitutive model; failure mode; impact loading; polypropylene.