Silver nanoparticles (NPs) are effective antibacterial agents; however, aggregation of NPs and uncontrolled release of Ag+ affect their efficiency and may pose a risk to the environment. To overcome these disadvantages, immobilization of Ag onto titanate nanotubes (TNTs) was investigated. This paper describes the physicochemical and antibacterial properties of silver incorporated titanate nanotubes (Ag/TNTs) prepared using five procedures and containing different Ag amounts (0.11-30.85 wt.%). The methods were (i) sol-gel followed by a hydrothermal process; (ii) photodeposition under ambient conditions; (iii) photodeposition under an inert atmosphere; (iv) NaBH4 reduction; and (v) electroless deposition after activation of TNTs with Sn2+. Depending on the synthesis procedure, the presence of metallic Ag NPs, AgO or AgCl was observed. The electroless method led to an additional deposition of SnO2 NPs. The antibacterial properties of Ag/TNTs were analyzed as a function of Ag content and released against Escherichia coli and Staphylococcus epidermidis. The best bactericidal properties exhibited Ag/TNTs prepared through the photodeposition process due to the higher interaction of exposed Ag NPs with bacteria. An increase of Ag loading resulted in improvement of antibacterial activity of Ag/TNTs although no direct correlation between silver content or release and inhibition of bacterial growth was found.
Keywords: Ag; Escherichia coli; Staphylococcus epidermidis; TNT; antibacterial; titanate nanotubes.