A high-performance nanofiltration (NF) membrane with simultaneously improved desalination and antifouling properties while maintaining regeneration ability is highly desirable in water treatment. Surface modification is an effective approach to enhance the performance of NF membranes. In the present study, a multifunctional thin-film composite NF membrane (Fe-TFC) was fabricated via coating a regenerable ferric ion-tannic acid (FeIII-TA) layer on the nascent polyamide membrane surface. The Fe-TFC membrane exhibited enhanced hydrophilicity, smaller pore size, and lower negative charge compared with the control membrane. The salt rejections and selectivity of divalent to monovalent ions were greatly improved with only a slight decrease in water permeability due to the presence of the coating layer. Meanwhile, dynamic fouling tests with humic acid demonstrated that the Fe-TFC membrane possessed an enhanced antifouling property and excellent flux recovery rate. After coating, the normalized water flux and flux recovery of the Fe-TFC membrane increased from 0.02 to 0.26 and 32.1 to 76.4% at the end of five cycles of fouling tests, respectively. In addition, the resultant membrane exhibited excellent durability and stability under harsh conditions for ∼10 days. Interestingly, the fouled coating layer can be easily removed by HCl cleaning and regenerated through an in situ strategy. Consequently, the regenerated membranes presented stable antifouling properties and desalination performance after several times of regeneration. It was demonstrated that the unique feature of FeIII-TA networks enables the coating layer to act as a protective layer for the underlying polyamide membrane, leading to the high performance of the composite membrane. This study provides a new insight for surface functionalization and easy regeneration of the TFC nanofiltration membrane in water treatment technology.
Keywords: antifouling capability; desalination performance; nanofiltration; regeneration; thin-film composite.