Here, butylene adipate-co-terephthalate/polypyrrole with nanohydroxyapatite (PBAT/PPy/nHAp) scaffolds were fabricated and characterized. The electrospinning process was carried out using 12 kV, a needle of 23 G, an infusion pump set at 0.3 mL/h, and 10 cm of distance. Afterwards, nHAp was directly electrodeposited onto PBAT/PPy scaffolds using a classical three-electrode apparatus. For in vivo assays (comet assay, acute and chronic micronucleus), 60 male albino Wistar rats with 4 groups were used in each test (n = 5): PBAT/PPy; PBAT/PPy/nHAp; positive control (cyclophosphamide); and the negative control (distilled water). Peripheral blood samples were collected from the animals to perform the comet test after 4 h (for damage) and 24 h (for repair). In the comet test, it was shown that the scaffolds did not induce damage to the % DNA tail and neither for tail length. After the end of 48 h (for acute micronucleus) and 72 h (for chronic micronucleus), bone marrow was collected from each rat to perform the micronucleus test. All of the produced scaffolds did not present genotoxic effects, providing strong evidence for the biological application of PBAT/PPy/nHAp scaffolds.
Keywords: Poly (butylene adipate-co-terephthalate); and comet assays; micronucleus; nanohydroxyapatite; nanotechnology; polypyrrole.