The development of materials based on renewable resources with enhanced mechanical and physicochemical properties is hampered by the abundance of hydrophilic groups because of their structural instability. Bio-inspired from the strong adhesion ability of mussel proteins, renewable and robust soy-based composite films were fabricated from two soybean-derived industrial materials: soluble soybean polysaccharide (SSPS) and catechol-functionalized soy protein isolate (SPI-CH). The conjugation of SPI with multiple catechol moieties as a versatile adhesive component for SSPS matrix efficiently improved the interfacial adhesion between each segment of biopolymer. The biomimetic adherent catechol moieties were successfully bonded in the polymeric network based on catechol crosslinking chemistry through simple oxidative coupling and/or coordinative interaction. A combination of H-bonding, strong adhesion between the SPI-CH conjugation and SSPS matrix resulted in remarkable enhancements for mechanical properties. It was found that the tensile strength and Young's modulus was improved from 2.80 and 17.24 MPa of unmodified SP film to 4.04 and 97.22 MPa of modified one, respectively. More importantly, the resultant films exhibited favorable water resistance and gas (water vapor) barrier performances. The results suggested that the promising way improved the phase adhesion of graft copolymers using catechol-functionalized polymers as versatile adhesive components.
Keywords: catechol functionalization; full utilization; interfacial adhesion; mechanical properties; mussel-inspired; soy based films.