In this paper, a novel method for preparing nanoparticle-polymer hybrid adsorbent was established. Laponite was dispersed in distilled water to form Laponite nanoparticles. These nanoparticles were pre-adsorbed by 2-acrylamido-2-methylpropane-sulfonic acid (AMPS) to improve their dispersion stability in chitosan solution. The nanoparticle-polymer hybrid adsorbent was prepared by copolymerization of chitosan, acrylamide, acrylic acid, AMPS, and Laponite nanoparticles. Four adsorbents were obtained and characterized by Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), and Brunauer-Emmett-Teller adsorption (BET). Additionally, the uptake capacities of Cu2+ using different samples were studied. Compared to the adsorbent without chitosan and Laponite components, the maximum uptake of the hybrid adsorbent increased from 0.58 to 1.28 mmol·g-1 and the adsorption equilibrium time of it decreased from more than 75 min to less than 35 min, which indicated that the addition of chitosan and Laponite could greatly increase the adsorption rate and capacity of polymer adsorbent. The effects of different experimental parameters-such as initial pH, temperature, and equilibrium Cu2+ concentration-on the adsorption capacities were studied. Desorption study indicated that this hybrid adsorbent was easy to be regenerated.
Keywords: Laponite; biosorbent; heavy metal removal; nanoparticle-polymer hybrids; rapid adsorption.