Poly(3-hydroxybutyrate⁻co⁻3-hydroxyvalerate) (PHBV) is a biodegradable polymer and has several potential applications. Herein, we have used a rich biomass resource, rice husk, to obtain rice husk nano-SiO₂ (RHNS) and prepared RHNS/PHBV composites by using hot-press molding. The results showed that the amorphous nature of spherical nano-SiO₂ particles with an average diameter of 40⁻80 nm was obtained. The tensile strength and flexural strength of the RHNS/PHBV-3 composite reached up to 23.515 and 75.669 MPa, respectively, corresponding to an increase of 33.65% and 15.54% as compared to pure PHBV. The enhanced mechanical properties of the RHNS/PHBV composite can be attributed to the uniform dispersion and strong interfacial bonding of RHNS with the PHBV matrix. In addition, the water absorption rate of the RHNS/PHBV composite increased from 0.26% to 0.35% and the water swelling ratio followed the given order in different directions: thickness > width > length. Furthermore, the initial degradation temperature and residual rate of combustion at 700 °C of the composites increased with higher content of RHNS, which represents the enhanced thermal stability of RHNS/PHBV composites. In summary, RHNS served as an excellent reinforcement and RHNS/PHBV composites have shown promising properties for various potential applications.
Keywords: PHBV; RHNS; SiO2; mechanical properties; rice-husk; thermal stability; water absorption.