In this study, corn straw (CS) was reduced in size using the superfine grinding process to generate powders with particles of varying sizes (9~16 μm). The lignin, hemicellulose, and cellulose content; particle size distribution; and scanning electron microscopy (SEM) of the CS samples were analyzed. Superfine CS, of varying particle sizes, was added to the starch-based films (SF) in various amounts. The resulting corn straw starch-based films (CS/SFs) appeared to have significantly different properties, compared to the original starch-based film (SF, p < 0.05). The power law model and Burger's model were used to investigate the dynamic mechanical analysis, which indicated that the mechanical properties of CS/SF performed better than that of SF, especially CS/SFs at 0.5⁻1.5 h ball milling and CS/SFs at a 15% addition amount. The power law model and Burger's model also presented a strong correlation with the experimental data (>0.90).
Keywords: corn straw; mechanical properties; starch-based film; superfine grinding.