Strong polyampholytes comprising cationic vinylbenzyl trimethylammonium chloride (VBTAC) bearing a pendant quaternary ammonium group and anionic sodium p-styrenesulfonate (NaSS) bearing a pendant sulfonate group were prepared via reversible addition-fragmentation chain-transfer polymerization. The resultant polymers are labelled P(VBTAC/NaSS)n, where n indicates the degree of polymerization (n = 20 or 97). The percentage VBTAC content in P(VBTAC/NaSS)n is always about 50 mol%, as revealed by ¹H NMR measurements, meaning that P(VBTAC/NaSS)n is a close to stoichiometrically charge-neutralized polymer. Although P(VBTAC/NaSS)n cannot dissolve in pure water at room temperature, the addition of NaCl or heating solubilizes the polymers. Furthermore, P(VBTAC/NaSS)n exhibits upper critical solution temperature (UCST) behavior in aqueous NaCl solutions. The UCST is shifted to higher temperatures by increasing the polymer concentration and molecular weight, and by decreasing the NaCl concentration. The UCST behavior was measured ranging the polymer concentrations from 0.5 to 5.0 g/L.
Keywords: RAFT; UCST; electrostatic interaction; polyampholyte.