Laser welding⁻brazing of 5A06 aluminum to Ti6Al4V titanium in a butt configuration was carried out to discuss the influences of welding parameters on dissimilar joint properties. The effects of laser offset, welding speed, and laser power on the spreading length of the molten aluminum liquid, interface fracture zone width (IFZW), fracture roughness, intermetallic compounds (IMCs) thickness, and tensile strength were also investigated. The microstructure and fracture of the joint were also studied. The results show that the tensile strength of the joint is not only influenced by the thickness and type of IMCs, but also influenced by the spreading ability of the aluminum liquid, the fracture area broken at the Ti/fusing zone (FZ) interface, and the relative area of the brittle and ductile fracture in FZ. A dissimilar butt joint with an IMC thickness of 2.79 μm was obtained by adjusting the laser offset, welding speed, and laser power to 500 μm, 11 mm/s and 1130 W, respectively. The maximum tensile strength of the joint was up to 183 MPa, which is equivalent to 83% of the tensile strength of the 5A06 aluminum alloy.
Keywords: aluminum; laser welding–brazing; tensile strength; titanium.