The Bi-SnO2/C electrocatalytic membrane was fabricated via a simple electrochemical reduction and hydrothermal method. Under the action of electric field, the Sn2+ and Bi3+ were firstly adsorbed and reduced to metallic Sn and Bi on the carbon membrane surface by cathodic reduction reaction, and the Bi-SnO2/C membrane was obtained subsequently through hydrothermal oxidation process. Confirmed by SEM, TEM, XRD, and XPS characterizations, the nano-Bi-SnO2 is homogeneously distributed on the membrane surface and is firmly attached to the carbon membrane via C-O-Sn chemical bond. Through CV, LSV, and EIS electrochemical analysis, the Bi-SnO2/C membrane possesses the higher electrocatalytic activity and stability than carbon membrane. Therefore, the Bi-SnO2/C membrane could continuously efficiently remove and inactivate Escherichia coli in water through flow-through mode. As a result, the sterilization efficiency can reach more than 99.99% under the conditions of cell voltage 4 V, flow rate 1.4 mL/min, and E. coli initial concentration 1.0 × 104 CFU/mL, owing to the synergistic effect of the membrane separation and electrocatalytic oxidation. Moreover, it was found that the oxidation groups of ⋅OH radicals generated by Bi-SnO2/C membrane play the crucial role for bactericidal performance. This work presents a low-cost, highly active, and stable electrocatalytic membrane towards continuous bacterial inactivation, which exhibits promising potential in water disinfection and is beneficial for practical large-scale applications.
Keywords: Bi-doped SnO2; E. coli inactivation; Electrocatalytic activity; Electrocatalytic membrane; Water treatment.