Carbon foam was prepared from carboxymethyl cellulose (CMC) and Ag, Al and carbon nanotubes (CNTs), and graphene was added to the foam individually, to investigate the enhancement effects on the thermal conductivity. In addition, we used the vacuum method to impregnate erythritol of the phase change material (PCM) into the carbon foam samples to maximize the latent heat and minimize the latent heat loss during thermal cycling. Carbon foams containing Ag (CF-Ag), Al (CF-Al), CNT (CF-CNT) and graphene (CF-G) showed higher thermal conductivity than the carbon foam without any nano thermal conducting materials (CF). From the variations in temperature with time, erythritol added to CF, CF-Ag, CF-Al, CF-CNT, and CF-G was observed to decrease the time required to reach the phase change temperature when compared with pure erythritol. Among them, erythritol added to CF-G had the fastest phase change temperature, and this was related to the fact that this material had the highest thermal conductivity of the carbon foams used in this study. According to differential scanning calorimetry (DSC) analyses, the materials in which erythritol was added (CF, CF-Ag, CF-Al, CF-CNT, and CF-G) showed lower latent heat values than pure erythritol, as a result of their supplementation with carbon foam. However, the latent heat loss of these supplemented materials was less than that of pure erythritol during thermal cycling tests because of capillary and surface tension forces.
Keywords: carbon foam; latent heat storage; nanomaterials; phase change material; thermal conductivity.