Metallic silver nanowires with high yield were synthesized using a modified seed mediated approach at room temperature. Ribbon-like nanostructures were obtained when the concentration of NaOH was lower and further increase of NaOH transformed it into long nanowires. These nanowires possess high aspect ratio, with length and diameter ~6.5 μm and 17 nm respectively. The surface enhanced Raman scattering activity of these nanowires was tested with three different probe molecules viz., crystal violet, malachite green and nile blue chloride using visible (514.4 nm) and near-infrared (784.8 nm) excitation lines. The minimum detection limits for crystal violet and nile blue chloride molecules were found to be down to 10-7 M with good linear responses, as evidenced by values of correlation coefficients, indicating their potential for a variety of applications such as sensing. Principal component analysis was performed with the surface enhanced Raman spectra in order to discriminate the dye molecules and their mixture, simultaneously. The first two principal components, which provided 69.80 and 27.93% of the total data variance, could be conveniently represented as a two dimensional PCA score plot. The score plot showed clear clustering of probe molecules and their mixture. The relative contribution of wavenumbers to each of the two principal components was identified by plotting the PCA loading matrix. These results further promote possibilities of quantification of multiplexed SERS detection and analysis.
Keywords: Loading plot; Principal component analysis; Score plot; Silver nanowires; Surface enhanced Raman scattering.
Copyright © 2019 Elsevier B.V. All rights reserved.