The incorporation of large π-conjugated ligands into metal-organic frameworks (MOFs) can introduce intriguing photophysical and electrochemical properties into the framework. However, these effects are often hindered by the strong π-π interaction and the low solubility of the arylated ligands. Herein, we report the synthesis of a porous zirconium-based MOF, Zr6(μ3-O)4(μ3-OH)4(OH)6(H2O)6(HCHC) (PCN-136, HCHC = hexakis(4-carboxyphenyl)hexabenzocoronene), which is composed of a hexacarboxylate linker with a π-conjugated hexabenzocoronene moiety. Direct assembly of the Zr4+ metal centers and the HCHC ligands was unsuccessful due to the low solubility and the unfavorable conformation of the arylated HCHC ligand. Therefore, PCN-136 was obtained from aromatization-driven postsynthetic annulation of the hexaphenylbenzene fragment in a preformed framework (pbz-MOF-1) to avoid π-π stacking. This postsynthetic modification was done through a single-crystal-to-single-crystal transformation and was clearly observable utilizing single -crystal X-ray crystallography. The formation of large π-conjugated systems on the organic linker dramatically enhanced the photoresponsive properties of PCN-136. With isolated hexabenzocoronene moieties as photosensitizers and Zr-oxo clusters as catalytic sites, PCN-136 was employed as an inherent photocatalytic system for CO2 reduction under visible-light irradiation, which showed increased activity compared with pbz-MOF-1.