Mn4+ activated LaMgAl11O19 (LMA/Mn4+) with red emitting phosphor was obtained by sintering under air conditioning. The X-ray diffraction pattern Rietveld refinement results reveal that three six-fold coordinated Al sites are substituted by Mn4+ ions. Furthermore, the chemical valence state of manganese in the LMA host was further confirmed through X-ray photoelectron spectroscopy (XPS) and electron paramagnetic resonance (EPR). Photoluminescence emission (PL) and excitation (PLE) spectra of LMA/Mn4+ as well as the lifetime were measured, and the 663 nm emission is ascribed to the ²Eg→⁴A2g from the 3d³ electrons in the [MnO₆]8- octahedral complex. The emission spectrum matches well with the absorption of phytochrome. Temperature-dependent PL spectra show that the color changes of the phosphor at 420 K are 0.0110 for Δx and -0.0109 for Δy. Moreover, doping Zn2+ and Mg2+ ions in the host enhances the emission intensity of Mn4+ ions. These results highlight the potential of LMA/Mn4+ phosphor for a light-emitting diode (LED) plant lamp.
Keywords: LED; Mn4+; luminescence; phosphor.