Sorption heat storage, as one of low-energy consuming technologies, is an approach to reduce CO₂ emissions. The efficiency of such technology is governed by the performance of the applied sorbents. Thus, sorbents with high water sorption capacity and regeneration temperature from 80 to 150 °C are required. Incorporation of hygroscopic salt such as calcium chloride into porous materials is a logical strategy for increasing the water sorption capacity. This work reports the study on the development of composites with PHTS (plugged hexagonal templated silicate) matrix with an average pore size of 5.7 nm and different amounts of calcium chloride (4, 10, 20 wt.%) for solar thermal energy storage. These composites were prepared by wetness incipient impregnation method. Structural properties were determined by X-ray diffraction (XRD), nitrogen physisorption, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). CaCl₂ was confined in micro- and mesopores of the matrix. The resulting CaCl₂-PHTS materials were used for water sorption at 40 °C, showing an increase of maximal water uptake with higher amount of calcium chloride from 0.78 g/g to 2.44 g/g of the dry composite. A small reduction in water uptake was observed after 20 cycles of sorption/desorption between temperatures of 140 °C and 40 °C, indicating good cycling stability of these composites under the working conditions.
Keywords: CaCl2-PHTS; composites; heat storage; structural properties; water sorption.