The aim of this in vitro study was to evaluate the alterations of a titanium surface after treatment with two different types of ultrasonic tips: conventional steel versus an innovative copper alloy silver-plated one. Twenty smooth-surface, grade IV unalloyed titanium discs were divided into two groups. The discs were ultrasonically instrumented and the scaler was connected with a loading machine. The surface morphology was examined using scanning electron microscopy (SEM) and fractal analysis of lacunarity was calculated to highlight the alteration of the surface using the two different tips. The SEM analysis showed different degrees of surface roughness between the two types of scaler tips. Moreover, these observations demonstrated that the new tip showed fewer irregularities on the disc's surface than the conventional steel tip. The statistical and fractal analysis showed a statistically significant difference between the two groups. Surface alterations of titanium induced by the conventional ultrasonic tips were much greater than those made by copper alloy silver plated tips. The presented results suggest that the use of this new ultrasonic tip may reduce the alterations on the implant surface during its use in dental practice.
Keywords: dental implant; in vitro; surface topography; titanium surface.