Background: Previous studies had reported that bond strength deteriorate over time following the dentin surface pretreatment with chlorhexidine. Therefore, further investigations are needed to evaluate the effect of other materials such as povidone iodine. The purpose of this study was to investigate the effects of 10% povidone-iodine pretreatment on the resin-dentin micro-tensile bond strength of a single bond adhesive system in permanent teeth over time, and compare it with 2% chlorhexidine.
Methods: Flat dentin surfaces were prepared in 63 extracted permanent teeth. Teeth were randomly assigned to a 10% povidone-iodine pretreatment, a 2% chlorhexidine pretreatment, or a control group. Composite resin blocks were built up over treated surfaces under pulp pressure simulation. The prepared specimens were assigned to three storage time, 24 h, 1 week, and 2 months. Samples were vertically sectioned to obtain specimens of 0.7 to 1.2 mm2 cross-sectional area.
Results: No significant reduction of bond strength of povidone iodine group was found among the three storage times (p = 0.477). A significant reduction of bond strength for both chlorhexidine and control groups was found in the three storage times (p < 0.001).
Conclusion: Povidone iodine pretreatment of etched dentin was effective in reducing the loss of bond strength over time, while the chlorhexidine pretreatment and negative control showed significant deterioration in micro-tensile bond strength over time in permanent teeth.
Keywords: Chlorhexidine; Matrix metalloproteinase; Micro-tensile bond strength; Povidone-iodine.