The lubrication performance of graphene used as additive in 4-n-pentyl-4'-cyanobiphyl liquid crystal (5CB) for steel/steel contacts was studied on a ball-on-plate tribotester. The friction test results show that when the graphene content in the 5CB was 0.15 wt.%, and the lubricant and friction pairs were heated to 44⁻46 °C before friction tests, the lubrication performance of the 5CB was most improved. Compared with pure 5CB, 5CB+0.15 wt.% graphene suspension reduced the friction coefficient and wear scar diameter by up to 70.6% and 41.3%, respectively. The lubrication mechanisms have been tentatively proposed according to the test results. We speculate that the excellent lubrication performance of graphene/5CB suspensions may be attributed to the low shear resistance adsorption layer formed by graphene and 5CB molecules on the sliding surfaces. As the protective layer, it not only prevents direct contact between the rough sliding surfaces but also is easy to slide.
Keywords: 5CB; graphene; lubricant additive; lubrication performance.