Hypothesis: Bionic superhydrophobicity including high contact angle, low sliding angle and nonstick property, combined with both strong pH and ultraviolet (UV) resistance, is difficult to simultaneously achieve for large-scale preparation of superhydrophobic surfaces by blending polymer with a nonreactive inorganic nanofiller.
Experiments: A series of high pH and UV-irradiation-resistant superhydrophobic nanocomposite films were prepared through UV-light-assisted chemical cross-linking among ternary components under nitrogen protection. Ethoxylated bisphenol A diacrylate, 2-(perfluorooctyl) ethyl acrylate, reactive thiol-coupled graphene nanosheets and photoinitiator were evenly mixed, followed by UV-irradiation curing.
Findings: Abundant 3D networks could be formed. A robust self-wrinkling surface morphology was formed due to a UV-curing-induced inner tension in the composites, 2D morphology-induced flexibility for graphene nanosheets and fluorine-bearing component-induced phase separation at the wetted surfaces. High roughness and use of the fluorine element endows the surfaces with superhydrophobicity and oleophobicity. A favorable nonstick performance was obtained. Superhydrophobicity could be maintained despite changing the film-forming substrate, pH of soaking solutions from 1 to 12, or use of a prolonged UV-irradiation time reaching 120 h. Therefore, both superhydrophobicity/oleophobicity and strong pH/UV resistance are finely balanced. This work might open up the way for large-scale fabrication of promising superhydrophobic surfaces.
Keywords: Fluorine; Graphene; Nanocomposite; Network; Oleophobic; Reactive; Superhydrophobic; Surface; Ultraviolet; Wrinkling.
Copyright © 2018. Published by Elsevier Inc.