In this study, bromelain was used to break soy protein molecules into polypeptide chains, and triglycidylamine (TGA) was added to develop a bio-adhesive. The viscosity, residual rate, functional groups, thermal behavior, and fracture surface of different adhesives were measured. A three-ply plywood was fabricated and evaluated. The results showed that using 0.1 wt% bromelain improved the soy protein isolate (SPI) content of the adhesive from 12 wt% to 18 wt%, with viscosity remaining constant, but reduced the residual rate by 9.6% and the wet shear strength of the resultant plywood by 69.8%. After the addition of 9 wt% TGA, the residual rate of the SPI/bromelain/TGA adhesive improved by 13.7%, and the wet shear strength of the resultant plywood increased by 681.3% relative to that of the SPI/bromelain adhesive. The wet shear strength was 30.2% higher than that of the SPI/TGA adhesive, which was attributed to the breakage of protein molecules into polypeptide chains. This occurrence led to (1) the formation of more interlocks with the wood surface during the curing process of the adhesive and (2) the exposure and reaction of more hydrophilic groups with TGA to produce a denser cross-linked network in the adhesive. This denser network exhibited enhanced thermal stability and created a ductile fracture surface after the enzymatic hydrolysis process.
Keywords: adhesive; bromelain; soy protein isolate; triglycidylamine; viscosity; water resistance.