For improving the adhesion property of ethylene-co-n-butyl acrylate copolymer (EBA) at ambient temperature, binary blends of EBA with 27 wt% n-butyl acrylate and different amounts (20⁻62 wt%) of low molecular weight hydrogenated glycerol rosin ester (ECH) resin have been prepared. The addition of glycerol rosin ester resin decreased the crystallinity and size of the ethylene domains of the EBA copolymer. The addition of up to 50 wt% (100 phr) ECH resin improved the compatibility with the EBA copolymer, whereas when more than 50 wt% (100 phr) ECH resin was added, the compatibility of the blends did not change but the viscoelastic properties were noticeably decreased. Furthermore, the compatibility was noticeably improved by adding only 20 wt% ECH resin although the best compromise between compatibility and viscoelasticity corresponded to the binary blend made with 43 wt% ECH resin. The EBA copolymer + ECH resin blends showed high tack (initial adhesion) at 25 °C and some of them even at 5 °C, and they have adequate 180° peel strength both to polar (polyethylene terephthalate-PET) and nonpolar (polypropylene-PP) substrate. Furthermore, all EBA copolymer + ECH resin blends showed high shear strength at 25 °C. Finally, the blend with 43 wt% ECH resin showed excellent pressure sensitive adhesive property exhibiting excellent creep, high tack, high 180° peel strength, and high single lap-shear strength.
Keywords: adhesion; compatibility; ethylene-co-n-butyl acrylate copolymer; glycerol rosin ester; pressure sensitive adhesive; tack.