As a promising energy-storage device, rechargeable Zn-air batteries have attracted considerable interests. Herein, a bifunctional oxygen electrode film prepared by adhering NiCo2 O4 nanosheets to a nitrogen and oxygen dual-doped carbon nanotubes film in a large scale is reported. The resulting self-supporting film electrode is multifunctional, which integrates a porous conducting structure for air diffusion and charge transfer, high-performance catalysts for oxygen reduction and evolution, and novel structural flexibility. The composite film demonstrates excellent oxygen reduction/evolution reaction catalytic activities with low Tafel slopes (50 mV dec-1 for oxygen reduction reaction; 92 mV dec-1 for oxygen evolution reaction). Without any additional current collector, gas diffusion layer, or binder, the obtained bifunctional film performs as an "all-in-one" air electrode in a Zn-air battery. A 50-cm-long cable-shaped Zn-air battery based on such a film air electrode exhibits high operating potentials (≈1.2 V at 0.25 mA cm-2 ), low charging-discharging overpotentials (≈0.7 V), and stable cycling performance. Moreover, the flexible cable Zn-air batteries show excellent stability under different deformation conditions. The proposed concept of constructing scalable, all-in-one, freestanding, and flexible air electrodes would pave the way to develop next-generation wearable and portable energy-storage devices.
Keywords: Zn-air batteries; all-in-one air electrodes; bifunctional catalysts; carbon nanotube films; large-scale.
© 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.