TMC-incorporated carbon nitride (CN) with hexagonal and quadrangle honeycomb-like structure and having periodic lattice defects linked by -CONH- bond was synthesized through combining the high calcination with the chemical condensation of melamine and 1,3,5-benzenetricarbonyl trichloride. The obtained CN has a tri-s-triazine ring and benzene ring skeleton, which makes it have excellent mechanical and thermal stability. The BET specific surface area was enhanced to about 125.6 m2/g, and the mean pore size is about 3.43 nm. This CN exhibited an excellent adsorption-enhanced photocatalytic performance.
Keywords: Carbon nitride materials; Melamine; Nanoparticles; Sintering.