Based on the results of nitrogen adsorption and dynamic vapour sorption as well as analysis by the Hailwood-Horrobin (H-H) model, the effects of γ-methacryloxypropyltrimethoxysilane (MPTS) on the agglomeration and moisture sorption properties of fumed silica particles were investigated. After adding various concentrations (2%, 4%, 6% and 8%) of MPTS, different degrees of silanization were obtained by showing various ─OH group contents on the silica surface, which resulted in silica agglomerates with different porous structures. The bigger mesopores in the unmodified silica agglomerates became smaller and finally disappeared after MPTS modification and the Bruanuer-Emmett-Teller surface area decreased more gradually with an increase in MPTS concentration. The H-H model fitted the sorption isotherms very well, and both hydrated water and dissolved water showed decreasing trends with the increase in MPTS concentration, showing reduced hygroscopicity. Up to 6% MPTS, the ─OH groups decreased with increasing MPTS concentration, as indicated by reduced Kh and W parameters, while at 8% MPTS an extensive self-condensation of MPTS occurred. Adsorption hysteresis appeared for moisture sorption on silanized silica, especially at low relative humidity values and at low MPTS concentrations, which could be explained by a synergistic effect of the surface ─OH group content and pore characteristics. These results could aid our understanding of the applications of silane-modified silica particles.
Keywords: Hailwood–Horrobin model; adsorption hysteresis; agglomerates; moisture adsorption; nitrogen adsorption; silanized silica particles.