Nanocrystal solar cells (NCs) allow for large scale solution processing under ambient conditions, permitting a promising approach for low-cost photovoltaic products. Although an up to 10% power conversion efficiency (PCE) has been realized with the development of device fabrication technologies, the open circuit voltage (Voc) of CdTe NC solar cells has stagnated below 0.7 V, which is significantly lower than most CdTe thin film solar cells fabricated by vacuum technology (around 0.8 V~0.9 V). To further improve the NC solar cells' performance, an enhancement in the Voc towards 0.8⁻1.0 V is urgently required. Given the unique processing technologies and physical properties in CdTe NC, the design of an optimized band alignment and improved junction quality are important issues to obtain efficient solar cells coupled with high Voc. In this work, an efficient method was developed to improve the performance and Voc of solution-processed CdTe nanocrystal/TiO₂ hetero-junction solar cells. A thin layer of solution-processed CdS NC film (~5 nm) as introduced into CdTe NC/TiO₂ to construct hetero-junction solar cells with an optimized band alignment and p-n junction quality, which resulted in a low dark current density and reduced carrier recombination. As a result, devices with improved performance (5.16% compared to 2.63% for the control device) and a Voc as high as 0.83 V were obtained; this Voc value is a record for a solution-processed CdTe NC solar cell.
Keywords: CdS; CdTe; TiO2; nanocrystal; solar cells; solution processed.