Dialdehyde cellulose (DAC) derived from α-cellulose by periodate oxidation was solubilized and utilized as a suitable crosslinking agent for poly(vinyl alcohol) (PVA). The crosslinking occurs between reactive aldehyde groups of DAC on the C2 and C3 carbons of anhydroglucose unit and hydroxyl groups on PVA backbone in the presence of acidic catalyst. Two catalyst systems based on diluted hydrochloric or sulfuric acid were tested. Their influence on the PVA/DAC network has been investigated by solid-state 13C NMR, XRD analysis and in the terms of network parameters and mechanical properties. Because DAC undergoes structural changes and decays with time, the role of DAC solution age (1, 14 and 28 days old) on material properties of formed PVA/DAC samples was studied as well. Outlined, even after 28 days after solution preparation, DAC exhibited the capability to act as an efficient crosslinker for PVA. The resulting material properties of PVA/DAC hydrogels were found to be dependent on the molecular weight of solubilized DAC closely related to its age and the choice of catalyst system. Furthermore, the DAC potential for PVA crosslinking was investigated in a broad concentration range. Besides, the DAC crosslinking efficiency was also compared to that of common crosslinking agent glutaraldehyde. The results showed different network topology of prepared hydrogels and exceptional crosslinking potential of DAC in comparison to glutaraldehyde, which is most likely related to DAC macromolecular character.
Keywords: Aging; Crosslinking; Dialdehyde cellulose; Glutaraldehyde; Network parameters; Poly(vinyl alcohol).
Copyright © 2018 Elsevier Ltd. All rights reserved.