Nanostructured polymer films with continuous, membrane-spanning pores from polymerizable hexagonal columnar discotic liquid crystals (LCs) were fabricated. A robust alignment method was developed to obtain homeotropic alignment of columns between glass surfaces by adding a small amount of a tri(ethylene glycol) modified analogue of the mesogen as a dopant that preferentially wets glass. The homeotropic LC alignment was fixated via a photoinitiated free radical copolymerization of a high-temperature tolerant trisallyl mesogen with a divinyl ester. Removal of the hydrogen-bonded template from the aligned columns afforded a nanoporous network with pores of nearly 1 nm in diameter perpendicular to the surface, and without noticeable collapse of the nanopores. The effect of pore orientation was demonstrated by an adsorption experiment in which homeotropic film showed a threefold increase in the initial uptake rate of methylene blue compared to planarly aligned films.
Keywords: adsorption; homeotropic alignment; liquid crystals; nanoporous membranes; polymer network.