A set of multi-segmented Fe/Cu nanowires were synthesized by a two-step anodization process of aluminum substrates and a pulsed electrodeposition technique using a single bath. While both Fe segment length and diameter were kept constant to (30 ± 7) and (45 ± 5) nm, respectively, Cu length was varied between (15 ± 5) and (120 ± 10) nm. The influence of the non-magnetic layer thickness variation on the nanowire magnetic properties was investigated through first-order reversal curve (FORC) measurements and micromagnetic simulations. Our analysis confirmed that, in the multi-segmented Fe/Cu nanowires with shorter Cu segments, the dipolar coupling between Fe segments controls the nanowire magnetic behavior, and its performance is like that of a homogenous Fe nanowire array of similar dimensions. On the other hand, multi-segmented Fe/Cu nanowires with larger Cu segments act like a collection of non-interacting magnetic entities (along the nanowire axis), and their global behavior is mainly controlled by the neighbor-to-neighbor nanodisc dipolar interactions.
Keywords: FORC; magnetic interactions; micromagnetic simulations; multi-segmented nanowires.