Highly energetic materials have received significant attention, particularly 2,4,6,8,10,12-hexanitro-2,4,6,8,10,12-hexaazaisowurtzitane (CL-20). However, the application of this material was limited due to its high sensitivity. It is well known that the shape, size, and structure of energetic materials (EMs) significantly influence their sensitivity. At present, there are several ways to reduce the sensitivity of CL-20, such as spheroidization, ultrafine processing, and composite technology. However, only one or two of the abovementioned methods have been reported in the literature, and the obtained sensitivity effect was unsatisfactory. Thus, we tried to further reduce the sensitivity of CL-20 by combining the above three methods. The as-prepared composite was precipitated from the interface between two solutions of water and ethyl acetate, and the composite was insensitive compared with other reported CL-20-based EMs. The H50 value for the composite ranged up to 63 cm. This approach opens new prospects for greatly reducing the sensitivity of high Ems.
Keywords: CL-20; PNCB; micro-scale spherical composite; ultrasound-assisted emulsion method.