Statement of problem: Acrylic resin overdenture bases usually fracture because of stress concentrations at the area of the abutments.
Purpose: The purpose of this study was to evaluate the reinforcing effect of bidirectional woven electrical glass (E-glass) fiber weaves with a different number of layers and different locations on the load-bearing capacity of simulated Locator-retained overdenture specimens.
Material and methods: Test specimens with a centrally located metal housing for a Locator stud attachment were fabricated from autopolymerizing acrylic resin (polymethylmethacrylate based) and reinforced with bidirectional woven E-glass fiber layers. The control group specimens were fabricated without fiber reinforcement. The 2L group had 2 layers of E-glass fiber weaves and was divided according to the fiber location within the specimens as follows: 2L-A subgroup with 2 fiber layers above the metal housing; 2L-N subgroup with 2 fiber layers adjacent to the housing; and 2L-A+2L-N subgroup with 2 fiber layers above and 2 fiber layers adjacent to the housing. The 4L group had 4 layers of E-glass fiber weaves and was divided according to the fiber location as follows: 4L-A subgroup with 4 fiber layers above the housing; 4L-N subgroup with 4 fiber layers adjacent to the housing; and 4L-A+4L-N subgroup with 4 fiber layers above and 4 fiber layers adjacent to the housing. Dry specimens were submitted to a 3-point static loading test, and the mean flexural strength, flexural modulus, and strain values were analyzed with 1-way ANOVA and Tukey post hoc tests (α=.05). Two-way ANOVA was conducted to detect the influence of the number and location of the reinforcing layers (α=.05).
Results: The results revealed a significant difference (P<.001) in flexural strength values between the control group (92.4 ±14 MPa) and the 2 subgroups, 4L-A (116 ±7.3 MPa) and 4L-A+4L-N (117.1 ±6 MPa), with a significant effect only from the number of the reinforcing layers (P<.001) and not the location (P=.153). No significant differences were found with flexural modulus (P=.195) and strain values (P=.174) among the tested groups.
Conclusions: The load-bearing capacity of a Locator-retained overdenture can be significantly increased by placing 4 layers of bidirectional woven E-glass fiber weaves either only above the metal housing or in both locations above and adjacent to the metal.