The notorious lithium (Li) dendrites and the low Coulombic efficiency (CE) of Li anode are two major obstacles to the practical utilization of Li metal batteries (LMBs). Introducing a dendrite-suppressing additive into nonaqueous electrolytes is one of the facile and effective solutions to promote the commercialization of LMBs. Herein, Li difluorophosphate (LiPO2F2, LiDFP) is used as an electrolyte additive to inhibit Li dendrite growth by forming a vigorous and stable solid electrolyte interphase film on metallic Li anode. Moreover, the Li CE can be largely improved from 84.6% of the conventional LiPF6-based electrolyte to 95.2% by the addition of an optimal concentration of LiDFP at 0.15 M. The optimal LiDFP-containing electrolyte can allow the Li||Li symmetric cells to cycle stably for more than 500 and 200 h at 0.5 and 1.0 mA cm-2, respectively, much longer than the control electrolyte without LiDFP additive. Meanwhile, this LiDFP-containing electrolyte also plays an important role in enhancing the cycling stability of the Li||LiNi1/3Co1/3Mn1/3O2 cells with a moderately high mass loading of 9.7 mg cm-2. These results demonstrate that LiDFP has extensive application prospects as a dendrite-suppressing additive in advanced LMBs.
Keywords: electrolyte additive; lithium dendrite suppression; lithium difluorophosphate; lithium metal battery; solid electrolyte interphase.