Microstructure and Mechanical Properties of TiC0.7N0.3-HfC-WC-Ni-Mo Cermet Tool Materials

Jiaojiao Gao; Jinpeng Song; Ming Lv

doi:10.3390/ma11060968

Microstructure and Mechanical Properties of TiC_0.7N_0.3-HfC-WC-Ni-Mo Cermet Tool Materials

Materials (Basel). 2018 Jun 8;11(6):968. doi: 10.3390/ma11060968.

Authors

Jiaojiao Gao^{1

2}, Jinpeng Song^{3

4}, Ming Lv^{5

6}

Affiliations

¹ School of Mechanical Engineering, Taiyuan University of Technology, Taiyuan 030024, China. gaojiaojiao1207@163.com.
² Shanxi Key Laboratory of Precision Machining, The Shanxi Science and Technology Department, Taiyuan University of Technology, Taiyuan 030024, China. gaojiaojiao1207@163.com.
³ School of Mechanical Engineering, Taiyuan University of Technology, Taiyuan 030024, China. songjinpeng@tyut.edu.cn.
⁴ Shanxi Key Laboratory of Precision Machining, The Shanxi Science and Technology Department, Taiyuan University of Technology, Taiyuan 030024, China. songjinpeng@tyut.edu.cn.
⁵ School of Mechanical Engineering, Taiyuan University of Technology, Taiyuan 030024, China. lvming@tyut.edu.cn.
⁶ Shanxi Key Laboratory of Precision Machining, The Shanxi Science and Technology Department, Taiyuan University of Technology, Taiyuan 030024, China. lvming@tyut.edu.cn.

Abstract

TiC_0.7N_0.3-HfC-WC-Ni-Mo cermet tool materials were fabricated by hot pressing technology at 1450 °C. The effects of WC (tungsten carbide) content on the microstructure and mechanical properties of TiC_0.7N_0.3-HfC-WC-Ni-Mo cermet tool materials were investigated. The results showed that the TiC_0.7N_0.3-HfC-WC-Ni-Mo cermets were mainly composed of TiC_0.7N_0.3, Ni, and (Ti, Hf, W, Mo)(C, N); there were three phases: a dark phase, a gray phase, and a light gray phase. The dark phase was the undissolved TiC_0.7N_0.3, the gray phase was the solid solution (Ti, Hf, W, Mo)(C, N) poor in Hf, W, and Mo, and the light gray phase was the solid solution (Ti, Hf, W, Mo)(C, N) rich in Hf, W, and Mo. The increase of WC content could promote the process of HfC to form a solid solution and the HfC formed a solid solution more easily with WC than with TiCN. The increase of the solid solution made the microstructure more uniform and the mechanical properties better. In addition, the Vickers hardness, flexural strength, and fracture toughness of the TiC_0.7N_0.3-HfC-WC-Ni-Mo cermet increased with the increase of WC content. When the content of WC was 32 wt %, the cermet obtained the optimal comprehensive mechanical properties in this investigation. The toughening mechanism of TiC_0.7N_0.3-HfC-WC-Ni-Mo cermet tool materials included solid solution toughening, particle dispersion toughening, crack bridging, and crack deflection.

Keywords: TiCN-HfC-WC cermet; hot-pressed sintering; mechanical properties; microstructure.