The present work shows the synthesis of nano-sized hybrid zeolitic imidazolate frameworks (ZIFs) with the rho topology based on a mixture of the linkers benzimidazole (bIm) and 4-methyl-5-imidazolecarboxaldehyde (4-m-5-ica). The hybrid ZIF was obtained by post-synthetic modification of ZIF-93 in a bIm solution. The use of different solvents, MeOH and N,N-dimethylacetamide (DMAc), and reaction times led to differences in the quantity of bIm incorporated to the framework, from 7.4 to 23 % according to solution-state NMR spectroscopy. XPS analysis showed that the mixture of linkers was also present at the surface of the particles. The inclusion of bIm to the ZIF-93 nanoparticles improved the thermal stability of the framework and also increased the hydrophobicity according to water adsorption results. N2 and CO2 adsorption experiments revealed that the hybrid material has an intermediate adsorption capacity, between those of ZIF-93 and ZIF-11. Finally, ZIF-93/11 hybrid materials were applied as fillers in polybenzimidazole (PBI) mixed matrix membranes (MMMs). These MMMs were used for H2 /CO2 separation (at 180 °C) reaching values of 207 Barrer of H2 and a H2 /CO2 selectivity of 7.7 that clearly surpassed the Robeson upper bound (corrected for this temperature).
Keywords: H2/CO2 separation; hybrid zeolitic imidazolate framework; membranes; polybenzimidazole; synthesis design.
© 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.