Alternative processing routes such as powder metallurgy, the extrusion of recycled chips, or equal channel angular pressing (ECAP) have been considered for effective methods of maintaining the high mechanical strength of Mg-Y-Zn alloys containing long-period stacking ordered structures with respect to the alloy processed by the conventional extrusion of as-cast ingots with the advantage of minimizing the yttrium content. A yield stress similar to that found for extruded Mg97Y₂Zn₁ alloy can be attained with only half of the usual yttrium and zinc additions thanks to the grain refinement induced by ECAP processing. The properties of Mg98.5Y₁Zn0.5 subjected to ECAP are maintained up to 200 °C, but superplastic behavior is found above this temperature when the alloy is processed through a powder metallurgy route.
Keywords: ECAP; LPSO-phase; magnesium alloys; mechanical properties; powder metallurgy.