In this study, as-cast Mg⁻6Sn⁻2Zn (wt.%) alloy was subjected to friction stir processing (FSP) and the microstructure and tensile properties of FSP Mg⁻6Sn⁻2Zn samples were investigated. It was found that, in the stir zone (SZ) of FSP Mg⁻6Sn⁻2Zn samples, α-Mg grains were significantly refined via dynamic recrystallization (DRX) and the Mg₂Sn phase was broken and partially dissolved. The microstructure in SZ was nonuniform and DRXed grains in the SZ-up regions were coarser than those in the SZ-down regions. Coarse broken Mg₂Sn particles were observed in the SZ-up regions, while only fine Mg₂Sn particles were observed in the SZ-down regions. Strong {0001} basal texture developed in the SZ regions of Mg⁻6Sn⁻2Zn samples after FSP. The increase of travel speed had little effect on the texture of different SZ regions. The ductility of FSP Mg⁻6Sn⁻2Zn samples was obviously improved, while the improvement in strength was negligible when compared to the as-cast sample. The tensile properties of FSP Mg⁻6Sn⁻2Zn samples were influenced by grain refinement, texture modification, and the breaking up and dissolution of the Mg₂Sn phase.
Keywords: Mg–Sn–Zn alloy; friction stir processing; microstructure; tensile properties; texture.