Convergent beam electron diffraction (CBED) in transmission electron microscopy (TEM) was applied to determine local carbon concentrations in low-carbon transformation-induced plasticity (TRIP) steels. High-order Laue-zone (HOLZ) lines were experimentally obtained for comparison with simulation results. A new procedure for calculating carbon content is thus proposed. Retained austenite (RA) is classified into three types by morphology; the relationship between the carbon content and the corresponding RA morphology is discussed based on CBED results. Furthermore, results of X-Ray diffractometry measurements are also used for comparison.
Keywords: CBED; TEM; TRIP steels; high-order Laue-zone (HOLZ) lines.