In this work, a new composite materials of graphene oxide (GO)-incorporated metal-organic framework (MOF)(UiO-66-NH₂/GO) were in-situ synthesized, and were found to exhibit enhanced high performances for CO₂ capture. X-ray diffraction (XRD), scanning electron microscope (SEM), N₂ physical adsorption, and thermogravimetric analysis (TGA) were applied to investigate the crystalline structure, pore structure, thermal stability, and the exterior morphology of the composite. We aimed to investigate the influence of the introduction of GO on the stability of the crystal skeleton and pore structure. Water, acid, and alkali resistances were tested for physical and chemical properties of the new composites. CO₂ adsorption isotherms of UiO-66, UiO-66-NH₂, UiO-66/GO, and UiO-66-NH₂/GO were measured at 273 K, 298 K, and 318 K. The composite UiO-66-NH₂/GO exhibited better optimized CO₂ uptake of 6.41 mmol/g at 273 K, which was 5.1% higher than that of UiO-66/GO (6.10 mmol/g). CO₂ adsorption heat and CO₂/N₂ selectivity were then calculated to further evaluate the CO₂ adsorption performance. The results indicated that UiO-66-NH₂/GO composites have a potential application in CO₂ capture technologies to alleviate the increase in temperature of the earth's atmosphere.
Keywords: UiO-66-NH2; carbon dioxide adsorption; graphene oxide (GO); metal-organic framework (MOF).