Synthesis and characterization of starch-g-poly(vinyl acetate-co-butyl acrylate) bio-based adhesive for wood application

Abstract

Enhancing the performance of wood adhesive is important for its industrial applications. Accordingly, we designed and demonstrated the use of two co-monomers vinyl acetate (VAc) and butyl acrylate (BA) for promoting the graft copolymerization while improving the bonding performance of wood adhesive. The results showed that the addition of co-monomers in the ratio of VAc/BA 6:4 (v/v, volume basis of VAc) could improve the shear strength to 6.68MPa and 3.32MPa in dry and wet states, respectively. ¹H-nuclear magnetic resonance (¹H NMR) and fourier transform infrared spectroscopy (FT-IR) analysis revealed successful graft copolymerization reaction while the morphologies were observed by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Furthermore, the grafting reaction and thermal stabilities of wood adhesive were analyzed by X-ray photoelectron spectroscopy (XPS) and thermogravimetric analysis (TGA). The results showed that the properties of wood adhesive could improve dramatically by using two co-monomers VAc and BA during the graft copolymerization reaction.

Keywords: Co-monomer; Starch; Wood adhesive.