Optical properties of poly-silicon material are investigated to be integrated in new silicon photonics devices, such as capacitive modulators. Test structure fabrication is done on 300 mm wafer using LPCVD deposition: 300 nm thick amorphous silicon layers are deposited on thermal oxide, followed by solid phase crystallization anneal. Rib waveguides are fabricated and optical propagation losses measured at 1.31 µm. Physical analysis (TEM ASTAR, AFM and SIMS) are used to assess the origin of losses. Optimal deposition and annealing conditions have been defined, resulting in 400 nm-wide rib waveguides with only 9.2-10 dB/cm losses.