The nanosized Bi-doped SnO2/reduced graphene oxide 3D hybrids have been synthesized via one-step hydrothermal method. The structures, morphologies, photocatalytic activities of the as-prepared samples were discussed, respectively. The formation mechanism of the as-prepared hybrids was also proposed. Experimental results indicated that the usage amount of Bi2Sn2O7 obviously affected the photocatalytic performance of the as-prepared products. When it was 450 mg, the as-prepared sample possessed the band gap energy of 1.9 eV and the photocatalytic efficiency of 90% in 210 min for degradation of rhodamine B solution. In addition, triethylene tetramine and the as-prepared carbon hydrogel could act as reductant to synergistically reduce Bi2Sn2O7 into Bi-doped SnO2 particles during the formation of the hybrids.