The presence of antibiotics in the water and wastewater has raised problems due to potential impacts on the environment and consequently their removal is of great importance. For this reason, this article aims to perform a study on the possibility of oxytetracycline (OTC) adsorption from aqueous medium by using the hydroxyapatite (HA) nanopowders as adsorbent materials. The hydroxyapatite nanopowders were synthesized by wet precipitation method by using orthophosphoric acid and calcium hydroxide as raw materials and investigated by XRD, SEM-EDX, FTIR and BET methods. The uncalcined and calcined hydroxyapatite samples have hexagonal crystal structure with crystal sizes smaller than 100nm and a specific surface area of 316m2/g and 139m2/g, respectively. The adsorption behavior of oxytetracycline, a zwitterionic antibiotic, on nanohydroxyapatite was investigated as a function of pH, contact time, adsorbent dosage and drug concentration by means of batch adsorption experiments. High oxytetracycline removal rates of about 97.58% and 89.95% for the uncalcined and calcined nanohydroxyapatites, respectively, were obtained at pH8 and ambient temperature. The adsorption process of oxytetracycline onto nanohydroxyapatite samples was found to follow a pseudo-second order and intraparticle diffusion kinetic models. The maximum adsorption capacities of 291.32mg/g and 278.27mg/g for uncalcined and calcined nanohydroxyapatite samples, respectively, have been found. The adsorption mechanism of OTC on the hydroxyapatite surface at pH8 can be established via surface complexation. The obtained results are indicative of good hydroxyapatite adsorption ability towards oxytetracycline drug.
Keywords: Adsorption; Hydroxyapatite; Oxytetracycline.
Copyright © 2018. Published by Elsevier B.V.