Rh/γ-Al₂O₃ catalysts were synthesized by both incipient wetness impregnation (IWI) and atomic layer deposition (ALD). The TEM images of the two catalysts showed that the catalyst from ALD had smaller particle size, and narrower size distribution. The surface chemical states of both catalysts were investigated by both XPS and X-ray Absorption Near Edge Structure (XANES), and the catalyst from IWI had higher concentration of Rh3+ than that from ALD. The catalytic performance of both catalysts was tested in the dry reforming of methane reaction. The catalyst from ALD showed a higher conversion and selectivity than that from IWI. The stability testing results indicated that the catalyst from ALD showed similar stability to that from IWI at 500 °C, but higher stability at 800 °C.
Keywords: X-ray techniques; XPS; atomic layer deposition; crystal growth; heterogeneous catalyst; microstructure.