The power conversion efficiency (PCE) of perovskite solar cells (PSCs) has now exceeded 20%; thus, research focus has shifted to establishing the foundations for commercialization. One of the pivotal themes is to curtail the overall fabrication time, to reduce unit cost, and mass-produce PSCs. Additionally, energy dissipation during the thermal annealing (TA) stage must be minimized by realizing a genuine low-temperature (LT) process. Here, tin oxide (SnO2 ) thin films (TFs) are formulated at extremely high speed, within 5 min, under an almost room-temperature environment (<50 °C), using atmospheric Ar/O2 plasma energy (P-SnO2 ) and are applied as an electron transport layer of a "n-i-p"-type planar PSC. Compared with a thermally annealed SnO2 TF (T-SnO2 ), the P-SnO2 TF yields a more even surface but also outstanding electrical conductivity with higher electron mobility and a lower number of charge trap sites, consequently achieving a superior PCE of 19.56% in P-SnO2 -based PSCs. These findings motivate the use of a plasma strategy to fabricate various metal oxide TFs using the sol-gel route.
Keywords: electron transport; perovskite solar cells; plasma annealing.
© 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.